17-4PH / SUS630 Rustfrit stål bar
| DIN | ASTM | AISI | UNS | JIS | Andet |
| 1.4542 | |||||
| X5CrNiCuNb16-4 | Klasse 630 | 630 | S17400 | SUS 630 | 17-4PH |
| AMS 5643 | |||||
| AMS 5622 | |||||
| Z6CNU17-04 | |||||
| 10705GU-GV |
Kemisk sammensætning ( %)
| C | Si | Mn | P | S | Cr | Ni | Mo | Andet |
|---|---|---|---|---|---|---|---|---|
| ≤ 0,07 | ≤ 1,00 | ≤ 1,00 | ≤ 0,040 | ≤ 0,030 | 15,0 ～ 17,0 | 3,00 ～ 5,00 | - | Cu 3,00 ～ 5,00 Nb + Ta 0,15 ~ 0,45 |
Mekaniske egenskaber
| Betingelse for varmebehandling | Trækstyrke Rm (MPa) | Udbytte Rp0,2 (MPa) | Forlængelse EN(%) | Reduktion i kryds sektion om brud Z (%) | Indvirkning AKV / AKU (J) | Brinell Hårdhed (HBW) |
|---|---|---|---|---|---|---|
| Udglødet | ≤ 1034 | ≤ 650 | 6,0 ～ 15,0 | 30,0 ～ 60,0 | - | ≤ 363 |
| H900 | ≥ 1380 | ≥ 1275 | ≥ 14,0 | ≥ 50,0 | ≥ 20 | ≤ 420 |
| H925 | ≥ 1310 | ≥ 1200 | ≥ 14,0 | ≥ 54,0 | ≥ 34 | ≤ 409 |
| H1025 | ≥ 1170 | ≥ 1140 | ≥ 15,0 | ≥ 56,0 | ≥ 47 | ≤ 352 |
| H1075 | ≥ 1140 | ≥ 1035 | ≥ 16,0 | ≥ 58,0 | ≥ 61 | ≤ 341 |
| H1100 | ≥ 1035 | ≥ 930 | ≥ 17,0 | ≥ 58,0 | ≥ 61 | ≤ 332 |
| H1150 | ≥ 1000 | ≥ 860 | ≥ 19,0 | ≥ 60,0 | ≥ 68 | ≤ 311 |
| H1150 + H1150 | ≥ 965 | ≥ 760 | ≥ 20,0 | ≥ 60,0 | ≥ 108 | ≤ 302 |
| H1150M | ≥ 860 | ≥ 585 | ≥ 22,0 | ≥ 68,0 | ≥ 135 | ≤ 277 |
Former og former:
Rund stang (diameter): 5,5 mm til 700 mm
Trådstang (diameter): 0,10 ~ 16 mm
Firkantet stang / flad stang: 5mm til 550mm
Stålbånd via koldvalset: T0.1 - 3mm X W5 - 650mm XL (eller i spoleform)
Smedet ring: OD200 ~ 1500 mm X ID150 ~ 1250 mm X H20 ~ 1250 mm
Tung / mellemplade via varmvalset: T50 - 200mm X W80- 1200mm X L1000-3000mm
Smedestykke: trinvise aksler med flanker / skiver / rør / snegle / donuts / terninger / andre forskellige former baseret på OEM.
Længde: Fast længde eller tilfældig længde eller baseret på kundens særlige krav.